Marsh, Joseph Jack (2017). Characterisation of crystallisation and melting in thermoplastic polymers using chip calorimetry. University of Birmingham. Ph.D.
|
Marsh17PhD.pdf
PDF - Accepted Version Download (52MB) |
Abstract
Fast scanning chip-calorimetry was used to explore the crystallisation and melting of three semi-crystalline polymers. The heating and cooling rates required to prevent crystallisation on cooling (from above Tm) and on re-heating (from below T\(_g\)) were determined as: 3,000 and 8,000˚C/s respectively in PCL, 75 and 250˚C/s respectively in PEEK and 10 and 100˚C/s respectively in PLA. The effect of the thermal lag was considered using indium as a standard and corrections of >5˚C were required at rates in excess of 5,000˚C/s.
As readily observed in conventional DSC (CDSC), PEEK exhibited a double melting endotherm and this was attributed to a melting-recrystallisation-melting process. The absence of recrystallisation above 250˚C allowed a Hoffman-Weeks analysis to be carried out over a broader temperature range than is general possible in CDSC. The interplay between thermal lag and re-crystallisation was analysed using heating rates covering 5 orders of magnitude. At an optimum heating rate of 1,500 ˚C/s, an equilibrium melting temperature of 359˚C was determined.
The consideration of thermal lag led to the measurement of diffusivity using the technique of laser flash apparatus (LFA). The high measurement speed in the LFA allowed a time and temperature resolved study of diffusivity in PLA. LFA, chip-calorimetry and CDSC were used in parallel to explore the cold-crystallisation kinetics of PLA and the development of the relatively unstable α’ crystals. A good correlation between chip-calorimetry and LFA was found, showing an Avrami exponent of 2 and nucleation constant of 6.58 x10\(^5\) and 6.87 x10\(^5\) respectively, corresponding to regime III.
| Type of Work: | Thesis (Doctorates > Ph.D.) | |||||||||
|---|---|---|---|---|---|---|---|---|---|---|
| Award Type: | Doctorates > Ph.D. | |||||||||
| Supervisor(s): |
|
|||||||||
| Licence: | ||||||||||
| College/Faculty: | Colleges (2008 onwards) > College of Engineering & Physical Sciences | |||||||||
| School or Department: | School of Metallurgy and Materials | |||||||||
| Funders: | None/not applicable | |||||||||
| Subjects: | T Technology > TN Mining engineering. Metallurgy | |||||||||
| URI: | http://etheses.bham.ac.uk/id/eprint/7299 |
Actions
 |
Request a Correction |
 |
View Item |
Downloads
Downloads per month over past year