Murray, Richard Cameron (2017). Design and development of a new class of intra-filament hybrid composite. University of Birmingham. Ph.D.

[img]
Preview
Murray17PhD.pdf
PDF - Accepted Version

Download (11MB)

Abstract

Two distinct techniques for “optimum” fibre spreading of 2400 Tex E-glass and 12K carbon fibre bundles were designed and developed in this research project. These techniques enabled increases in fibre bundle width of 956% and 1121% for E-glass and carbon fibre bundles respectively. These values surpass anything reported in the literature.
Tensile testing was conducted on dry fibre bundles in the as-received and spread state. A reduction in the tensile failure stress and Weibull survival probability was observed with an increase in gauge length. The effect of spreading was determined to be statistically significant at a gauge length of 100 mm; however it was not significant at a gauge length of 50 mm.
Composites were manufactured using as-received or spread fibre bundles and their properties analysed and compared. The composites manufactured using spread fibre bundles were significantly thinner than those manufactured using as-received fibre bundles. In hybrid composites the degree of mixing of the two reinforcing fibre types was greater than has been reported in the literature. The overall conclusion from this study is that the utilisation of spread E-glass and carbon fibre bundles can be used as a means for enhancing the apparent failure strain of carbon fibre composites.

Type of Work: Thesis (Doctorates > Ph.D.)
Award Type: Doctorates > Ph.D.
Supervisor(s):
Supervisor(s)EmailORCID
Fernando, GerardUNSPECIFIEDUNSPECIFIED
Licence:
College/Faculty: Colleges (2008 onwards) > College of Engineering & Physical Sciences
School or Department: School of Metallurgy and Materials
Funders: Other, Engineering and Physical Sciences Research Council
Other Funders: Defence Science and Technology Laboratory, UK
Subjects: T Technology > TN Mining engineering. Metallurgy
URI: http://etheses.bham.ac.uk/id/eprint/7283

Actions

Request a Correction Request a Correction
View Item View Item

Downloads

Downloads per month over past year