Melting point depression in biodegradable polyesters

Murphy, Shona (2011). Melting point depression in biodegradable polyesters. University of Birmingham. M.Res.


Download (15MB)


Investigation into the crystallisation kinetics and melting point depression of poly(L-lactideco-meso-lactide) with approximately 3.3% D-lactide content (PLA 3051D) was undertaken. The rate of crystallisation was too slow for a crystallisation exotherm to be detected by the DSC, therefore hot-stage microscopy was used as an alternative method to characterise the crystallisation behaviour. Light intensity with time during isothermal crystallisation of a thin polymer film (<15μm) was measured. The results were normalised in order to calculate crystallisation half-life (t0.5). From half-life calculations, the optimal crystallisation temperature was found to be 118°C. By replacing the light dependant resistor with a digital camera, the diameter growths of individual spherulites could be measured minute-by-minute. Using the results obtained through hot-stage microscopy, re-processing of PLA could be carried out to restore the original crystallinity at Tmax 118°C. Plots showing % crystallinity with storage time at 118°C indicated a storage time of 2 hours was required to restore the crystallinity to 40%. Studies using the high pressure DSC found that with increasing CO2 pressure up to 60 bar, the melting point decreased from 152 to 142°C . An alternative biodegradable polymer, polycaprolactone CAPA 6800 was investigated with high pressure DSC as a comparison polymer to polylactic acid. Similarly to PLA, the melting point of PCL showed a significant reduction (55 to 40°C) when soaked with increasing pressures of CO2.

Type of Work: Thesis (Masters by Research > M.Res.)
Award Type: Masters by Research > M.Res.
College/Faculty: Colleges (2008 onwards) > College of Engineering & Physical Sciences
School or Department: School of Metallurgy and Materials
Funders: None/not applicable
Subjects: T Technology > TN Mining engineering. Metallurgy
T Technology > TA Engineering (General). Civil engineering (General)


Request a Correction Request a Correction
View Item View Item


Downloads per month over past year