Fendoni, Alessandro (2010)
M.Res. thesis, University of Birmingham.
The corrosion behaviour of a AA2050T34-FSW was examined as a function of post weld heat treatment condition. Immersion tests in 0.1 M Nac1 and G110 intergranular tests were performed and the corrsion morphology and the depth of attacks in the different regions of the weld were investigated using FEG/SEM. Polarisation measuresments in the different regions of the weld and long term OCP for the full weld were taken and results were correlated with immersion test observations.
This unpublished thesis/dissertation is copyright of the author and/or third parties. The intellectual property rights of the author or third parties in respect of this work are as defined by The Copyright Designs and Patents Act 1988 or as modified by any successor legislation. Any use made of information contained in this thesis/dissertation must be in accordance with that legislation and must be properly acknowledged. Further distribution or reproduction in any format is prohibited without the permission of the copyright holder.
Repository Staff Only: item control page