Improved sol based ceramic moulds for use in investment casting

Jones, Samantha (1993). Improved sol based ceramic moulds for use in investment casting. University of Birmingham. Ph.D.

[img]
Preview
Jones93PhD1.pdf
PDF - Accepted Version

Download (13MB)
[img]
Preview
Jones93PhD2.pdf
PDF - Accepted Version

Download (18MB)
[img]
Preview
Jones93PhD3.pdf
PDF - Accepted Version

Download (37MB)

Abstract

An investigation has been carried out into the mechanisms of failure of silica bonded investment casting moulds, with the aim of reducing failure rates for larger components. The analysis begins with a detailed microstructural examination of a current commercial mould system using scanning electron microscopy and other allied analysis techniques. The mould structure is shown to be nonuniform and unpredictable, with poor packing of the ceramic constituents leading to a non-uniform porosity network. The structure and distribution of the binder is also established and this indicates that the major load bearing points within the mould consist of thin areas of silica. As such, the overall performance of the mould is directly related to that of the silica itself. This binder is shown to contain impurity elements leached from the ceramic filler at various stages during mould manufacture. These elements alter the phase composition and thermal properties of the binder.

Mould temperature profiles for a range of casting sizes have been measured and used to illustrate the relationship between metal weight and maximum temperature attained within the mould section. The profiles are also used to investigate the creep response of silica based binders. It is found that a combination of high temperatures and creep within the silica phase is responsible for the casting defects found with larger components. From these observations, a prediction is made regarding failure mechanisms and suggested remedial action. The thermal properties of several commercial water based binders are evaluated and the suitability of each as an alternative binder is discussed.

Type of Work: Thesis (Doctorates > Ph.D.)
Award Type: Doctorates > Ph.D.
Supervisor(s):
Supervisor(s)EmailORCID
Marquis, PeterUNSPECIFIEDUNSPECIFIED
Licence:
College/Faculty: Faculties (to 1997) > Faculty of Engineering
School or Department: School of Metallurgy and Materials
Funders: Science and Technology Facilities Council
Subjects: T Technology > TN Mining engineering. Metallurgy
T Technology > TS Manufactures
URI: http://etheses.bham.ac.uk/id/eprint/788

Actions

Request a Correction Request a Correction
View Item View Item

Downloads

Downloads per month over past year